Hastelloy B2
Hastelloy B2 Forging
Triton Metal is one of the leading manufacturer, suppliers and exporters of high quality Hastelloy B2 in Mumbai, India. Compared to other manufacturing process, Hastelloy B2 Metal forging is mainly focused on producing some of the strongest manufactured parts. It’s not just limited to iron and steel forging but as well as other metals also. Compared to other manufacturing process, Hastelloy B2 forging is mainly focused on producing some of the strongest manufactured parts. It’s not just limited to iron and steel forging but as well as other metals also.
Once the manufacturing process is completed, the manufactured product undergoes the process of Inspection. Which is one of the important aspects of metal forging manufacture, all the manufactured parts are being checked for defects under this process. It helps us to deliver a flawless products to our customer.
Triton Metal manufacture Hastelloy B2 Forgings as per international and national standards and other standards that include ASTM, ASME, and API. The size of these forgings range from ½ NB to 250 NB and length of these forgings is 2mm to 40mm. Hastelloy B2 Forgings raw material used for the manufacturing process is well-tested and inspected by inspection agencies and quality experts. They offer quality approval and certificate mentioning products quality and capability. Moreover, to sustain its quality they are packed in wooden cases or boxes marked with companies name, size, length, and specification, standard and part number.
Chemical Composition, %
- C…………………………………………….…………0.02 max.
- Ni………………………………………..…………Bal
- Si………………………………………………..………….0.1 max.
- N……………………………….…………………Bal
- S………………………..………….0.03 max.
- Mn……………………………………………..……….1.0 max.
- P………………………………………….……….0.04 max.
- Cr……………………………….………………………1.0 max.
- Mo……………………………………….………..26 – 30.
Hastelloy B2 Circle
Hastelloy B2 Circle are being supplied, manufactured and traded by Triton Metal to our esteemed patrons in best possible rates. Hastelloy B2 Rings (UNS N10276) can be forged, hot-upset and impact extruded. Oxyacetylene welding should be avoided due to possibility of carburization. Alloy B2 Circle resists chloride stress corrosion cracking even in boiling magnesium chloride. Alloy B2 Rings has excellent resistance to pitting and stress corrosion cracking. Some of its great features include: High strength, Durability, Thermal resistance, and more. Our offered array of Hastalloy B2 Circle is used in different industries for a wide range of applications. The offered Hastalloy B2 Rings are widely used in automobile, cement, aviation and marine industries.
Chemical Composition, %
- C…………………………………………….…………0.02 max.
- Ni………………………………………..…………Bal
- Si………………………………………………..………….0.1 max.
- N……………………………….…………………Bal
- S………………………..………….0.03 max.
- Mn……………………………………………..……….1.0 max.
- P………………………………………….……….0.04 max.
- Cr……………………………….………………………1.0 max.
- Mo……………………………………….………..26 – 30.
Hastelloy B2 Round Bars
Hastelloy B2 chemically consists of elements like nickel, molybdenum & chromium as its primary alloying material along with a small addition of tungsten. Hastelloy B2 welding rod is considered to be one of the premier corrosion resistant materials available for process industries in the market. One of the benefits of using the Hastelloy B2 rod is its excellent resistance to corrosion in both oxidizing as well as reducing environments. The high contents of both the elements, molybdenum and chromium along with the combination of the added tungsten, in the alloy is known to make the 2.4819 Alloy C 276 highly resistant to chlorine related stress corrosion cracking. These elements in the alloy also aid the ASTM B574 UNS N10276 in its resistance to general corrosion like pitting & crevice corrosion.
Chemical Composition, %
- C…………………………………………….…………0.02 max.
- Ni………………………………………..…………Bal
- Si………………………………………………..………….0.1 max.
- N……………………………….…………………Bal
- S………………………..………….0.03 max.
- Mn……………………………………………..……….1.0 max.
- P………………………………………….……….0.04 max.
- Cr……………………………….………………………1.0 max.
- Mo……………………………………….………..26 – 30.
Physical Constants and Thermal Properties
Some physical constants and thermal properties of Hastelloy B2 are shown in Tables. Low temperature thermal expansion, based on measurements made by the National Bureau of Standards.
Physical Constants
- Density, lb/cu in……………………….……..………..0.305
- gram/cc………………………..………………….8.44
- Melting Range, °F……………………………….……….2350-2460
- °C…………………………………………1290-1350
- Specific Heata ,
- Btu/lb°F (J/kg°C) 0°F (-18°C)…………………………0.096 (402)
- 70°F (21°)……….………………..0.098 (410)
- 200°F (93°C)…………..………………0.102 (427)
- 400°F (204°C)……………………………0.109 (456)
- 600°F (316°C)…………………………….0.115 (481)
- 800°F (427°C)…………………………….0.122 (511)
- 1000°F (538°C)…………..………………0.128 (536)
- 1200°F (649°C)…………………………..0.135 (565)
- 1400°F (760°C)…………………………..0.141 (590)
- 1600°F (871°C)……………..……………0.148 (620)
- 1800°F (982°C)…………………….…….0.154 (645)
- 2000°F (1093°C)…………………..……..0.160 (670)
- Permeability at 200 Oersted (15.9 kA/m)…….………..1.0006
- Curie Temperature, °F…………………………………………..<-320
- °C……………………….…………………..-196
Specifications
UNS N10665
ASTM B335 ASME SB335
ASTM B333
ASTM B333 ASME SB333
ASTM B366 ASME SB366
ASTM B564
A5.14 ERNiMo-7
ASME SFA 5.11(ENiMo-7) AWS A5.11 (ENiMo-7)
ASTM B622 ASME SB622
ASTM B619 ASME SB619
ASTM B626 ASME SB626
ASME SFA 5.14(ENiMo-7)
2.4617