Alloy 20

Alloy 20 Forging

Triton Metal is one of the leading manufacturer, suppliers and exporters of high quality Alloy 20 Forging in Mumbai, India. Compared to other manufacturing process, Alloy 20 Metal forging is mainly focused on producing some of the strongest manufactured parts. It’s not just limited to iron and steel forging but as well as other metals also. Compared to other manufacturing process, Alloy 20 Forging is mainly focused on producing some of the strongest manufactured parts. It’s not just limited to iron and steel forging but as well as other metals also.

Once the manufacturing process is completed, the manufactured product undergoes the process of Inspection. Which is one of the important aspects of metal forging manufacture, all the manufactured parts are being checked for defects under this process. It helps us to deliver a flawless products to our customer.

Triton Metal manufacture Alloy 20 Forging as per international and national standards and other standards that include ASTM, ASME, and API. The size of these forgings range from ½ NB to 250 NB and length of these forgings is 2mm to 40mm. Alloy 20 Forging raw material used for the manufacturing process is well-tested and inspected by inspection agencies and quality experts. They offer quality approval and certificate mentioning products quality and capability. Moreover, to sustain its quality they are packed in wooden cases or boxes marked with companies name, size, length, and specification, standard and part number.

Chemical Composition, %

Ni32 – 38
FeBal
Cr19 – 21
Cu3 – 4
Mo2 – 3
Cr1.0 max
Nb0.1 – 0.3
C0.02 max
Mn0.04 max
S1 – 2
P0.02 max
S0.005 max
Si0.7 max

Alloy 20 Circle

Alloy 20 Circle are being supplied, manufactured and traded by Triton Metal to our esteemed patrons in best possible rates. Alloy 20 can be forged, hot-upset and impact extruded. Oxyacetylene welding should be avoided due to possibility of carburization. Alloy 20 Circle resists chloride stress corrosion cracking even in boiling magnesium chloride. Alloy 20 Rings has excellent resistance to pitting and stress corrosion cracking. Some of its great features include: High strength, Durability, Thermal resistance, and more. Our offered array of Alloy 20 Circle is used in different industries for a wide range of applications. The offered Alloy 20 Rings are widely used in automobile, cement, aviation and marine industries.

Chemical Composition, %

Ni32 – 38
FeBal
Cr19 – 21
Cu3 – 4
Mo2 – 3
Cr1.0 max
Nb0.1 – 0.3
C0.02 max
Mn0.04 max
S1 – 2
P0.02 max
S0.005 max
Si0.7 max

Alloy 20 Round Bars

Alloy 20 chemically consists of elements like nickel, molybdenum & chromium as its primary alloying material along with a small addition of tungsten. Alloy 20 welding rod is considered to be one of the premier corrosion resistant materials available for process industries in the market. One of the benefits of using the Alloy 20 rod is its excellent resistance to corrosion in both oxidizing as well as reducing environments. The high contents of both the elements, molybdenum and chromium along with the combination of the added tungsten, in the alloy is known to make the 2.4819 Alloy C 276 highly resistant to chlorine related stress corrosion cracking. These elements in the alloy also aid the ASTM B574 UNS N10276 in its resistance to general corrosion like pitting & crevice corrosion.

Chemical Composition, %

Ni32 – 38
FeBal
Cr19 – 21
Cu3 – 4
Mo2 – 3
Cr1.0 max
Nb0.1 – 0.3
C0.02 max
Mn0.04 max
S1 – 2
P0.02 max
S0.005 max
Si0.7 max

Physical Constants

Density: 0.292 lb/in3, (8.08 g/cm3)

Modulus of Elasticity (E): At 70°F (20°C): 28.0 x 103 ksi (193 GPa)

Modulus of Rigidity (G): At 70°F (20°C): 11.0 x 103 ksi (76 GPa)

Coefficient of Expansion: 8.2 µin/in-°F (70-212°F)
14.7 µm/m-°C (25-100°C)

Electrical Resistivity: 53.5 µohm-in, (135.9 µohm-cm)

Thermal Conductivity: 85 Btu-in/ft2-hr-°F, 12.3 W/m-°C

Specifications

BS3072 NA18, QQ-N-286, DIN 17750, ISO 6208
BS3072 NA18, QQ-N-286, DIN 17750, ISO 6208
BS3072 NA18, QQ-N-286, DIN 17750, ISO 6208
AMS 4676, BS3076 NA18, ASTM B 865, DIN 17752, QQ-N-286, ISO 9723
AMS 4676, ISO 6208, ASTM B 865, DIN 17752, QQ-N-286
BS3076, NA18, DIN 17753, QQ-N-286, ISO 9724
DIN 17754, QQ-N-286, ISO 9725
UNS N05500, BS6076 NA13, Alloy K-500, Werkstoff Nr. 2.4375, MIL-N-24549, NACE MR-01-75

Types of Alloy

Alloy 20

Alloy 286