Hastelloy C276

Hastelloy C276 Forging

Triton Metal is one of the leading manufacturer, suppliers and exporters of high quality Hastelloy C276 in Mumbai, India. Compared to other manufacturing process, Hastelloy C276 Metal forging is mainly focused on producing some of the strongest manufactured parts. It’s not just limited to iron and steel forging but as well as other metals also. Compared to other manufacturing process, Hastelloy C276 forging is mainly focused on producing some of the strongest manufactured parts. It’s not just limited to iron and steel forging but as well as other metals also.

Once the manufacturing process is completed, the manufactured product undergoes the process of Inspection. Which is one of the important aspects of metal forging manufacture, all the manufactured parts are being checked for defects under this process. It helps us to deliver a flawless products to our customer.

Triton Metal manufacture Hastelloy C276 Forgings as per international and national standards and other standards that include ASTM, ASME, and API. The size of these forgings range from ½ NB to 250 NB and length of these forgings is 2mm to 40mm. Hastelloy C276 Forgings raw material used for the manufacturing process is well-tested and inspected by inspection agencies and quality experts. They offer quality approval and certificate mentioning products quality and capability. Moreover, to sustain its quality they are packed in wooden cases or boxes marked with companies name, size, length, and specification, standard and part number.

Chemical Composition, %

  • Nickel…………………………………………….…………58.0 min.
  • Chromium………………………………………..…………0.10mX
  • Iron………………………………………………..………….5.0 max.
  • Molybdenum……………………………….…………………8.0-10.0
  • Niobium (plus Tantalum)………………………..………….3.15-4.15
  • Carbon……………………………………………..……….0.10 max.
  • Manganese………………………………………….……….0.50 max.
  • Silicon……………………………….………………………0.50 max.
  • Phosphorus……………………………………….………..0.015 max.
  • Sulfur…………………………………..……….…..……..0.015 max
  • Aluminum…………………………………………………..0.40 max.
  • Titanium……………………………….……………………0.40 max.
  • Cobalta ……………………………………………………….1.0 max.

Hastelloy C276 Circle

Hastelloy C276 Circle are being supplied, manufactured and traded by Triton Metal to our esteemed patrons in best possible rates. Hastelloy C276 Rings (UNS N10276) can be forged, hot-upset and impact extruded. Oxyacetylene welding should be avoided due to possibility of carburization. Alloy C276 Circle resists chloride stress corrosion cracking even in boiling magnesium chloride. Alloy C276 Rings has excellent resistance to pitting and stress corrosion cracking. Some of its great features include: High strength, Durability, Thermal resistance, and more. Our offered array of Hastelloy C276 Circle is used in different industries for a wide range of applications. The offered Hastelloy C276 Rings are widely used in automobile, cement, aviation and marine industries.

Chemical Composition, %

  • Nickel…………………………………………….…………58.0 min.
  • Chromium………………………………………..…………0.10mX
  • Iron………………………………………………..………….5.0 max.
  • Molybdenum……………………………….…………………8.0-10.0
  • Niobium (plus Tantalum)………………………..………….3.15-4.15
  • Carbon……………………………………………..……….0.10 max.
  • Manganese………………………………………….……….0.50 max.
  • Silicon……………………………….………………………0.50 max.
  • Phosphorus……………………………………….………..0.015 max.
  • Sulfur…………………………………..……….…..……..0.015 max
  • Aluminum…………………………………………………..0.40 max.
  • Titanium……………………………….……………………0.40 max.
  • Cobalta ……………………………………………………….1.0 max.

Hastelloy C276 Round Bars

Hastelloy C276 chemically consists of elements like nickel, molybdenum & chromium as its primary alloying material along with a small addition of tungsten. Hastelloy c276 welding rod is considered to be one of the premier corrosion resistant materials available for process industries in the market. One of the benefits of using the Hastelloy c276 rod is its excellent resistance to corrosion in both oxidizing as well as reducing environments. The high contents of both the elements, molybdenum and chromium along with the combination of the added tungsten, in the alloy is known to make the 2.4819 Alloy C 276 highly resistant to chlorine related stress corrosion cracking. These elements in the alloy also aid the ASTM B574 UNS N10276 in its resistance to general corrosion like pitting & crevice corrosion.

 

Chemical Composition, %

  • Nickel…………………………………………….…………58.0 min.
  • Chromium………………………………………..…………20.0-23.0
  • Iron………………………………………………..………….5.0 max.
  • Molybdenum……………………………….…………………8.0-10.0
  • Niobium (plus Tantalum)………………………..………….3.15-4.15
  • Carbon……………………………………………..……….0.10 max.
  • Manganese………………………………………….……….0.50 max.
  • Silicon……………………………….………………………0.50 max.
  • Phosphorus……………………………………….………..0.015 max.
  • Sulfur…………………………………..……….…..……..0.015 max
  • Aluminum…………………………………………………..0.40 max.
  • Titanium……………………………….……………………0.40 max.
  • Cobalta ……………………………………………………….1.0 max.

Physical Constants and Thermal Properties

Some physical constants and thermal properties of Hastelloy C276 are shown in Tables. Lowtem perature thermal expansion, based on measurements made by the National Bureau of Standards.

Physical Constants

  • Density, lb/cu in……………………….……..………..0.305
  •             gram/cc………………………..………………….8.44
  • Melting Range, °F……………………………….……….2350-2460
  •                              °C…………………………………………1290-1350
  • Specific Heata ,
  • Btu/lb°F (J/kg°C) 0°F (-18°C)…………………………0.096 (402)
  •                                     70°F (21°)……….………………..0.098 (410)
  •                               200°F (93°C)…………..………………0.102 (427)
  •                             400°F (204°C)……………………………0.109 (456)
  •                             600°F (316°C)…………………………….0.115 (481)
  •                             800°F (427°C)…………………………….0.122 (511)
  •                           1000°F (538°C)…………..………………0.128 (536)
  •                           1200°F (649°C)…………………………..0.135 (565)
  •                           1400°F (760°C)…………………………..0.141 (590)
  •                           1600°F (871°C)……………..……………0.148 (620)
  •                           1800°F (982°C)…………………….…….0.154 (645)
  •                          2000°F (1093°C)…………………..……..0.160 (670)
  • Permeability at 200 Oersted (15.9 kA/m)…….………..1.0006
  • Curie Temperature, °F…………………………………………..<-320
  •                                     °C……………………….…………………..-196

Specifications

UNS N10276
AMS 5750
WS 2.4819
ASTM B574, ASME SB574 Bar Products
ASTM B575, ASME SB575 Plate, Sheet and Strip
ASTM B619, ASME SB619 Welded Pipe
ASTM B622, ASME SB622 Seamless Tubing
ASTM B626, ASME SB 626 Welded Tubing
ASTM B366, ASME SB 366 Wrought Corrosion Resistant Fittings CR HC 276, Wrought ANSI Pressure Fitting-WPHC276
ASTM B564 Forgings
AWS A 5.14, ASME SA 5.14 Welding Wire (ER NiCrMo-4)
AWS A 5.11, ASME SA 5.11 Covered Electrodes (E NiCRMo-4)
NACE MR-01-75
Inconel C276 (Trademark)
AMS 5750 (Hastelloy C, UNS N10002)
ASTM B751
Werkstoff Nr. 2.4819
DIN 17744, DIN 17750, DIN 17751 and DIN 17752,VRC276

Types of Hastelloy

Hastelloy C276

Hastelloy C22

Hastelloy B2